| BiOcclus® N |
|
Technical data |
| Compositions in |
weight-% |
| Gold/Platin metals |
97,8 |
| Gold (Au) |
85,6 |
|
Platin (Pt) |
11,9 |
|
Zinc (Zn) |
1,6 |
|
Niob (Nb) |
0,4 |
|
Ferric (Fe) |
0,2 |
|
Iridium (Ir) |
0,1 |
| Rhodium (Rh) | 0,2 |
|
| Melting range (°C) 1040 - 1115 |
| Average linear CTE* (µm/m× K) 14,4 (25 - 500 °C) 14,6 (25 - 600 °C) |
| Vickers hardness (HV 5) w 200 a 220 b 205 |
| 0,2 %-yield strength** (N/mm2) a 520 b 500 |
| Tensile strength** (N/mm2) a 630 b 605 |
| Elongation** (%) a 6 b 7 |
|
Density (g/cm3) 19,2 |
|
* coefficient of thermal expansion |
| ||||
 |
 |
 |
|
 |